Physical Properties
物理性质
|
Metric
公制数据
|
English
英制数据
|
Comments
测试方法
|
|
Density
密度
|
1.40
g/cc
|
0.0506
lb/in³
|
DAM; ISO 1183
|
|
Linear Mold Shrinkage, Flow
线性收缩率
/
流动
|
0.0030
cm/cm
@Thickness 2.00 mm |
0.0030
in/in
@Thickness 0.0787 in |
Parallel; DAM; ISO 294-4
|
|
Linear Mold Shrinkage, Transverse
线性收缩率
/
横向
|
0.0070
cm/cm
@Thickness 2.00 mm |
0.0070
in/in
@Thickness 0.0787 in |
Normal; DAM; ISO 294-4
|
|
Mechanical Properties
力学性能
|
Metric
公制数据
|
English
英制数据
|
Comments
测试方法
|
|
Tensile Strength at Break
断裂拉伸强度
|
200
MPa
@Temperature 23.0 °C |
29000
psi
@Temperature 73.4 °F |
DAM; ISO 527
|
|
Elongation at Break
断裂伸长率
|
3.5 %
@Temperature 23.0 °C |
3.5 %
@Temperature 73.4 °F |
DAM; ISO 527
|
|
Tensile Modulus
拉伸模量
|
11.0
GPa
@Temperature 23.0 °C |
1600
ksi
@Temperature 73.4 °F |
DAM; ISO 527
|
|
Flexural Modulus
弯曲弹性模量
|
10.0
GPa
@Temperature 23.0 °C |
1450
ksi
@Temperature 73.4 °F |
DAM; ISO 178
|
|
Izod Impact, Notched
悬臂梁缺口冲击强度
(ISO)
|
13.0
kJ/m²
@Temperature -40.0 °C |
6.19
ft-lb/in²
@Temperature -40.0 °F |
DAM; ISO 180/1A
|
|
15.0
kJ/m²
@Temperature 23.0 °C |
7.14
ft-lb/in²
@Temperature 73.4 °F |
DAM; ISO 180/1A
|
|
|
Charpy ImPAct, Notched
夏比缺口冲击
|
1.20
J/cm²
@Temperature -40.0 °C |
5.71
ft-lb/in²
@Temperature -40.0 °F |
DAM; ISO 179/1eA
|
|
1.40
J/cm²
@Temperature 23.0 °C |
6.66
ft-lb/in²
@Temperature 73.4 °F |
DAM; ISO 179/1eA
|
|
|
Electrical Properties
|
Metric
公制数据
|
English
英制数据
|
Comments
测试方法
|
|
Volume ResiSTivity
体积电阻率
|
2.00e+18
ohm-cm
@Temperature 23.0 °C |
2.00e+18
ohm-cm
@Temperature 73.4 °F |
DAM; IEC 60093
|
|
Surface Resistance
表面电阻
|
4.00e+15
ohm
@Temperature 23.0 °C |
4.00e+15
ohm
@Temperature 73.4 °F |
DAM; IEC 60093
|
|
Thermal Properties
热性能
|
Metric
公制数据
|
English
英制数据
|
Comments
测试方法
|
|
Deflection Temperature at
热变形温度
1.8 MPa (264 psi)
|
250
°C
|
482
°F
|
DAM; ISO 75-1/-2
|