Physical Properties
物理性质
|
Metric
公制数据
|
English
英制数据
|
Comments
测试方法
|
|
Density
密度
|
1.49 g/cc
|
0.0538 lb/in³
|
DAM; ISO 1183
|
|
Filler Content
填料含量
|
43 %
|
43 %
|
DAM
|
|
Water Absorption
吸水率
|
2.2 %
@Thickness 1.00 mm, Temperature 23.0 °C |
2.2 %
@Thickness 0.0394 in, Temperature 73.4 °F |
Equilibrium 50%RH; DAM; ISO 62, Similar to
|
|
7.6 %
@Thickness 1.00 mm, Temperature 23.0 °C |
7.6 %
@Thickness 0.0394 in, Temperature 73.4 °F |
Saturation, immersed; DAM; ISO 62, Similar to
|
|
|
Linear Mold Shrinkage, Flow
线性收缩率
/
流动
|
0.0030 cm/cm
@Thickness 2.00 mm |
0.0030 in/in
@Thickness 0.0787 in |
Parallel; DAM;ISO294-4
|
|
Linear Mold Shrinkage, Transverse
线性收缩率
/
横向
|
0.0090 cm/cm
@Thickness 2.00 mm |
0.0090 in/in
@Thickness 0.0787 in |
Normal; DAM; ISO 294-4
|
|
Mechanical Properties
力学性能
|
Metric
公制数据
|
English
英制数据
|
Comments
测试方法
|
|
Tensile Strength at Break
断裂拉伸强度
|
160 MPa
@Temperature 23.0 °C |
23200 psi
@Temperature 73.4 °F |
50%RH; ISO 527
|
|
225 MPa
@Temperature 23.0 °C |
32600 psi
@Temperature 73.4 °F |
DAM; ISO 527
|
|
|
Elongation at Break
断裂伸长率
|
2.5 %
@Temperature 23.0 °C |
2.5 %
@Temperature 73.4 °F |
DAM; ISO 527
|
|
3.5 %
@Temperature 23.0 °C |
3.5 %
@Temperature 73.4 °F |
50%RH; ISO 527
|
|
|
Tensile Modulus
拉伸模量
|
11.0 GPa
@Temperature 23.0 °C |
1600 ksi
@Temperature 73.4 °F |
50%RH; ISO 527
|
|
14.0 GPa
@Temperature 23.0 °C |
2030 ksi
@Temperature 73.4 °F |
DAM; ISO 527
|
|
|
Izod Impact, Notched
悬臂梁缺口冲击强度
(ISO)
|
14.0 kJ/m²
@Temperature 23.0 °C |
6.66 ft-lb/in²
@Temperature 73.4 °F |
DAM; ISO 180/1A
|
|
16.0 kJ/m²
@Temperature 23.0 °C |
7.61 ft-lb/in²
@Temperature 73.4 °F |
50%RH; ISO 180/1A
|
|
|
Charpy Impact Unnotched
夏比缺口试样冲击
|
9.00 J/cm²
@Temperature 23.0 °C |
42.8 ft-lb/in²
@Temperature 73.4 °F |
DAM; ISO 179/1eU
|
|
9.50 J/cm²
@Temperature 23.0 °C |
45.2 ft-lb/in²
@Temperature 73.4 °F |
50%RH; ISO 179/1eU
|